Company Consolidated companies Products Field service Download Contact News   About us Corporate policy   Allgemein Ausbildung Aktuelles   KIESOW DR. BRINKMANN Detmold KIESOW DR. BRINKMANN Berlin Prolectro Frankreich Prolectro Shanghai Metallchemie Austria Metallchemie Poland Metallchemie Hungary Sales partner   Grinding/Polishing Pre-Treatment Processes Electroplating Passivations Phosphating Waste Water Chemicals Anodes News   Compounds and Emulsions Polishing and Buffing Wheels / Brushes Belts/Tapes Germany Europe leer   Address Inquiry form Approach

Products  |  Grinding/Polishing  |  Polishing and Buffing Wheels / Brushes Polishing and Buffing Wheels / Brushes We can supply polishing and buffing wheels in a range of common sizes up to 1200 mm in diameter. We only use selected, tightly woven, tear resistant cotton cloth. This top quality material is then enhanced through a chemical treatment, which greatly improves the performance and life of our polishing and buffing wheels. Providing an added advantage of a reduction in the amount of buffing compounds or emulsion required to be used. By virtue of the many different forms of construction we employ, we are able to adapt to our customers needs, including the production of “tailor-made” products. Our sisal buffing wheels and brushes are made from long fibre raw material which can be supplied in the natural form or with different impregnations as required. A special line in our range, to produce a satin finish, is the supply of corrugated or laminated wheels made with a Scotch-Brite material (a fibrous pad with a cutting/polishing property). Abrasive rings, matting disks and matting rings Our products are made up of a nylon fleece with embedded abrasive grain, they come in different ring constructions and are used for light sanding, trimming, cleaning (incl. paint removal) as well as for various finishing techniques (pressing, matting). By using different abrasive grains varying results from coarse to very fine can be achieved. Mainly red fleece with aluminum oxide grain is used. Gray fleece contains the harder silica carbide grain. Aluminum oxide A 002 = A 80, extra coarse, approx. 80 grit A 004 = A 100, coarse, approx. 100 grit A 006 = A 180, medium, approx. 180 grit A 007 = A 280, fine, approx. 280-320 grit     Silica carbide S 004 = S 100, coarse, approx. 100 grit S 006 = S 180, medium, approx. 180 grit S 007 = S 400, fine, approx. 280-400 grit S 008 = S 600, very fine, approx. 500-600 grit S 009 = ultra fine, approx. 900 grit Density respective hardness of the matting disks and rollers are influenced by the number of lamellae. For special applications, the number of lamellae can be customized. We offer the following standard versions: Hardness 5 - LD - Low density - soft Hardness 7 - MD - Medium density - standard Hardness 8 - HD - High density - hard A rotation speed of 15m/sec. should not be exceeded as excessive heat will cause the fleece to leave a residue that can only be removed by additional sanding. A lower speed will create a coarser matting picture. High application pressure will create higher heat, leading to premature wear of the disc. News Place your order easily! For your convenience simply send your or to: bestellung@kiesow.org [mehr...] PROSEAL NP 300 - Passivation for Zinc Deposits PROSEAL NP 300 is a liquid concentrate which produces a blue to yellow film on zinc layers that have [mehr...] SURFASEAL WL 150 - Sealing for Chromated Parts Our product is a liquid, yellowish concentrate which provides a clear organic protection coating, [mehr...]

Sitemap  |  Imprint  |  GTC Realisation LOUIS INTERNET